Luster

Lusterless

Theoretical spreading rate

160g/m2, 8.13m2/L (calculated by 40μm dry film, excluding loss)

Specific gravity:

About 1.30

Drying time

23±2℃: surface dry≤4h, hard dry≤24h

Flash point

30℃

Storage period

12 months

Construction Instruction

Mixing ratio

Single canned

Maturing time

Ready to use when being opened and stirred evenly.

Service life

Unlimit

Construction method

High pressure siphon spray, air spray, manual brushing, roller painting.

Diluent

Diluent for X-7 epoxy coating

The largest amount of dilution

High pressuresiphon spray

Air spray

Manual brushing, roller painting

5%

5%

5%

Spray orifice

0.43~0.48mm

2.0~2.5mm

_

Spray pressure

12~15Mpa

0.3~0.4 Mpa

_

Tool washing

Diluent for X-7 epoxy coating.

Film coating thickness

Wet film: 120μm, dry film:50μm

Coating interval

Surface treatment

*Steel with oxide skin: treated with shot-blasting or spraying to reach Class Sa 2 of Swedish de-rusting standard;

*Steel without oxide skin: polished with pneumatic or power-driven elastic grinding discs up to Class St 3;

*Steel coated with Workshop primer: conduct second rust cleaning with slight sand blasting or pneumatic (power-driven) elastic grinding discs to reach Class St 3 of Swedish de-rusting standard.

Construction condition

Substrate temperature shall be more than dew point above 3℃, relative humidity shall be less than 85%;

Prior primer

Ethylene phosphating primer, zinc-rich epoxy Workshop primer, epoxy zinc powder Workshop primer, zinc-rich epoxy primer, inorganic zinc silicate primer, etc.

Finishing paint

Alkyd resin coating, phenolic resin coating, etc.

Packing Specification

Container of 20 liters can load 25kg.

Safety guide

Avoid inhaling solvent vapors and painting mist for long term, skin and eye may not contact with the product.

Forced ventilation shall be provided when applying the paint in confined spaces or stagnant air, although in good ventilation, protection tools shall be worn.

Annotation

＊Above-said thickness of dry film and wet film refers to the index while implementing the high-pressure siphon spray;

＊Relevant data in this instruction is obtained from laboratory, the actual product may be slightly different from it;

＊If above data is changed, the data is based on the latest instruction, without prior notification.