Luster

Semi-gloss

Theoretical spreading rate

270g/m2, 4.44m2/L (calculated by 125μm dry, excluding loss)

Specific gravity:

About 1.20

Drying time

Substrate temperature

5℃

20℃

30℃

Surface dryness

8h

4h

2h

Actual dryness

48h

24h

16h

Fully cured

14d

7d

5d

Flash point

Tan:22℃   Black:21℃

Storage period

12 months

Construction Instruction

Mixing ratio

Component A(paint)：Component B(curing agent) =20：4

Maturing time

23 ±2℃：0.5-1h

Service life

23 ±2℃：8h

Construction method

High pressure siphon spray，air spray, manual spray, roller spray

Diluent

X-7 epoxy diluent

Maximal dilution amount

High pressure siphon spray<5%; air spray<10%; manual spray, roller spray<5%

Spray orifice

High pressure siphon spray0.4~0.5mm; air spray2.0~3.0mm

Spray pressure

High pressure siphon spray20~30Mpa; air spray0.3~0.4Mpa

Tool washing

X-7 epoxy diluent

Film coating thickness

Wet film225μm, dry film125μm

Coating interval

Substrate temperature

5℃

20℃

30℃

The shortest

48h

24h

2h

The longest

14d

7d

3d

Surface treatment

Oxide skin steel

they shall be conducted the treatment of Shot blasting or Sand blasting ,meeting the Swedish derusting standard Sa2.5 level

No oxide skin steel

they can be conducted the treatment of Shot blasting or Sand blasting ,meeting the Swedish derusting standard Sa2.5 level or can be polished by pneumatic and electric tools to meet St2 level

Steel coated with shop primer

They need to be derusted for second times, the broken shop primer and polluted materials shall be eliminated clean, meeting the Swedish derusting standard St3level

Construction condition

The substrate temperature must over 3℃ than usual ,relative humidity must over 85%; when constructional substrate temperature is less than 5℃, epoxy and hardener will not be reacted, theconstruction shall be banned.

Prior primer

Epoxy zinc-rich shop primer, epoxy zinc powder shop primer, epoxy Rusty red shop primer, inorganic zinc silicate shop primer, and epoxy micaceous iron antirust paint can also be painted directly on the surface of steel which met the antirust quality of Sa2.5 level.

Finishing paint

Chlorinated rubber asphalt antirust paint, acrylic antifouling paint, chlorinated rubber long-term antifouling paint, self-polishing long-term antifouling paint, chlorinated rubber high- strength long-term antifouling paint, no tin polishing long-term antifouling paint, etc.

Packing Specification

Component A:20 liters containersper20kg components

Component B: 5 liters containersper 4kg components

Considerations

*Temperature>30℃ when respray with the paint film stuck on hand, the effect of respray is best.

*If in the excess of the biggest respray interval or coating paint, operators shall polish the surface of previous pass paint film first, and coat in order to keep the adhesion within layers.

Safety guide

*Avoiding inhalation of vapor or mist, skin and eyes shall not be contacted with this product. In the process of construction, the forced ventilation shall be provided especially in the place which is in narrow and stagnant air condition. The protective gear shall be provided in the execution of construction.

Annotation

＊Above-said thickness of dry film and wet film refers to the index while implementing the high-pressure air-free spray;

＊Relevant data in this instruction is obtained from laboratory, the actual product may be slightly different from it;

＊If above data is changed, the data is based on the latest instruction, without prior notification.