Luster

Lightless

Theoretical spreading rate

80g/m2, 16.25m2/L (calculated in 40μm dry film, excluding the loss)

Specific gravity:

About 1.30

Drying time

23±2℃: surface dryness≦4h, solid dryness≦24h

Flash point

35℃

Storage period

12 months

Construction Instruction

Mixing ratio

Canned by single pot

Maturing time

Use immediately after opening and stirring uniformly

Service life

Unlimit

Construction method

High-pressure siphon spray; normal spray;  manual painting;  roller coating  

Diluent

X-6Alkyd coatingdiluent

Maximal dilution amount

Spray orifice

Spray pressure

Tool washing

X-6Alkyd coatingdiluent

Film coating thickness

Wet film: 60μm                     Dry film: 40μm

Coating interval

Surface treatment

＊Oxide coating steel: it is required to be subjected to shotblasting or sandblasting treatment so as to reach Grade Sa2 of Sweden Derusting Standard;

＊Non-oxide coating steel: it is required to be polished by pneumatic or electric tool so as to reach Grade St3 of Sweden Derusting Standard.

＊Steel coated with primer in the workWorkshop: it is required to be subjected to secondary derusting so as to reach Grade St3 of Sweden Derusting Standard.

Construction condition

The temperature of substrate must be 3 ℃ higher than dewing point, and the relative humidity must be less than 85%.

Prior primer

Epoxy rich zinc primer, epoxy rusty red workWorkshop primer, in organic rich zinc primer, Alkyd rusty red anti-rust paint,  Alkyd red lead anti-rust paint

Finishing paint

Alkyd enamel paint, Alkyd tempered paint

Packing Specification

25Kg/20L per barrel

Safety guide  

Avoid breathing solvent steam or paint fog for a long term; the skin and eye can’t contact this product; while constructing in the narrow place or poorly ventilated place, the forced ventilation must be provided; while constructing, the protective articles should be worn.

Annotation

＊Above-said thickness of dry film and wet film refers to the index while implementing the high-pressure siphon spray;

＊Relevant data in this instruction is obtained from laboratory, the actual product may be slightly different from it;

＊If above data is changed, the data is based on the latest instruction, without priornotification.