Luster

Lightless

Theoretical spreading rate

180g/m2, 11.10m2/L (calculated in 40μm dry film, excluding the loss)

Specific gravity:

About 2.0

Drying time

23±2℃: surface dryness≦4h, solid dryness≦24h

Flash point

38℃

Storage period

12 months

Construction Instruction

Mixing ratio

Canned by single pot

Maturing time

Use immediately after opening and stirring uniformly

Service life

Unlimit

Construction method

Manual painting;  roller coating  

Diluent

X-6 Alkyd coating diluent

Maximal dilution amount

5%

Tool washing

X-6 Alkyd coating diluent

Film coating thickness

Wet film: 95μm                     Dry film: 60μm

Coating interval

Surface treatment

＊If it is coated directly on the steel, the steel is required to be subjected to shot blasting or sandblasting treatment  so as to reach Grade Sa2 of Sweden Derusting Standard, or the manual derusting reaches  Grade St3;

＊The primer surface in the workWorkshop is required to be subjected to secondary derusting so as to reach Grade St3 of Sweden Derusting Standard.

Construction condition

The temperature of substrate must be 3℃ higher than dewing point, and the relative humidity must be less than 85%.

Finishing paint

Alkyd enamel paint,alkyd tempered paint;alkyd rusty red anti-rust paint, Alkyd micaceous iron anti-rust paint.

Packing Specification

25Kg/20L per barrel

Considerations

＊This coating contains the heavy pigment particle, while constructing , this coating can be utilized after uniformly stirring thoroughly;

＊There is red lead inside paint film, it is inadvisable to be used in the sealed cabin where the fire work calibration must be conducted so as to prevent lead poisoning;

＊The red lead paint film is inadvisable to expose in the air for long term, otherwise, the paint film easily whitens or discolors.

Safety guide  

Avoid breathing solvent steam or paint fog for a long term; the skin and eye can’t contact this product; while constructing in the narrow place or poorly ventilated place, the forced ventilation must be provided; while constructing, the protective articles should be worn.

Annotation

＊Above-said thickness of dry film and wet film refers to the index while implementing the high-pressure siphon spray;

＊Relevant data in this instruction is obtained from laboratory, the actual product may be slightly different from it;

＊If above data is changed, the data is based on the latest instruction, without prior notification.