Luster

Semi-gloss

Theoretical spreading rate

125-156g/m2, 8.00m2/L (calculated by40μm dry film, excluding loss)

Specific gravity:

About 1.00-1.25

Drying time

(23±2℃) surface dry ≤2h, hard dry≤8h

Flash point

38℃

Storage period

12 months

Construction Instruction

Mixing ratio

Single canned

Maturing time

Ready to use after opening and stirring well

Service life

Unlimit

Construction method

High pressure siphon spray, air spray, manual brushing, roller spray.

Diluent

Diluents for X-14 chlorinated rubber coating.

The largest amount of dilution

High pressure siphon spray

Air spray

Manual brushing, roller spray

5%

10%

3%

Spray orifice

0.4~0.5mm

2.0~2.5mm

_

Spray pressure

12~15Mpa

0.3~0.4 Mpa

_

Tool washing

Diluents for X-14 chlorinated rubber coating.

Film coating thickness

Wet film: 125μm, dry film: 40μm

Coating interval

Surface treatment

If the preceding paint has been contaminated, take proper measurements to remove grease, dust, and also diluent for the preceding paint can be used to scrub.

Construction condition

Substrate temperature shall be more than dew point above 3℃, relative humidity shall be less than 85%.

Prior primer

Chlorinated rubber aluminum powder mastic antirust paint, chlorinated rubber iron red mastic antirust paint, epoxy resin antirust paint, etc.

Packing Specification

Container of 20 liters can load 20kg.

Safety guide

Avoid inhaling solvent vapors and spray mist for long term, skin and eye may not contact with the product.

Forced ventilation shall be provided when applying the paint in confined spaces or stagnant air, although in good ventilation, protection tools shall be worn.

Annotation

＊Above-said thickness of dry film and wet film refers to the index while implementing the high-pressure air-free spray;

＊Relevant data in this instruction is obtained from laboratory, the actual product may be slightly different from it;

＊If above data is changed, the data is based on the latest instruction, without prior notification.