Luster

Semi-gloss

Theoretical spreading rate

175-220g/m2, 5.71m2/L (calculated by 50μm dry, excluding loss)

Specific gravity:

1.00-1.25

Drying time

23 ±2℃：Surface dryness≤2h  Solid dryness≤8h

Flash point

25℃

Storage period

12 months

Construction Instruction

Mixing ratio

Single canned

Maturing time

Open and stir

Service life

Unlimit

Construction method

High pressure siphon spray, air spray, manual spray, roller spray

Diluent

X-15 acrylic coating diluent

High pressure siphon spray

Air spray

Manual spray, roller spray

Maximal dilution amount

5%

10%

3%

Spray orifice

0.4~0.5mm

2.0~2.5mm

-

Spray pressure

12~15Mpa

0.3~0.5Mpa

-

Tool washing

X-15 acrylic coating diluent

Film coating thickness

175μm for wet film, 75μm for dry film

Coating interval

Substrate temperature

0℃

20℃

30℃

The shortest

24h

8h

6h

The longest

Unlimit

Surface treatment

If the former primer has been polluted, the oil, dust shall be eliminated by proper method and can also be scrubbed by this paint diluent.

Construction condition

The substrate temperature must over 3℃ than usual point ,relative humidity must less than 85%.

Prior primer

Chlorinated rubber resin antirust paint, epoxy resin antirust paint.

Packing Specification

20 liters containers can load 20kg components

Safety guide

Avoiding inhalation of vapor or mist, skin and eyes shall not be contacted with this product. In the process of construction, the forced ventilation shall be provided especially in the place which is in narrow and stagnant air condition. The protective gear shall be provided in the execution of construction.

Annotation

＊Above-said thickness of dry film and wet film refers to the index while implementing the high-pressure air-free spray;

＊Relevant data in this instruction is obtained from laboratory, the actual product may be slightly different from it;

＊If above data is changed, the data is based on the latest instruction, without prior notification.