Luster

No gloss

Theoretical spreading rate

Rusty red:130g/m2, 10m2/L (calculated by 100μm dry, excluding loss)

Gray: 150g/m2, 10m2/L (calculated by 100μm dry, excluding loss)

Specific gravity:

Rusty red: about 1.32

Gray: about 1.51

Drying time

23±2℃：surface dryness≤4h, actual dryness≤24h

Fully cured

23±2℃：7d

Flash point

15℃

Storage period

12 months

Construction Instruction

Mixing ratio

Rusty red Component A(paint)：Component B(curing agent) =25：1.5

Gray Component A(paint)：Component B(curing agent) =24：4

Maturing time

23 ±2℃：0.5-1h

Service life

23 ±2℃：8h

Construction method

High pressure siphon spray，air spray, manual spray, roller spray

Diluent

Galvanized Plate Special Primer diluent

Maximal dilution amount

High pressure siphon spray<5%; air spray<10%; manual spray, roller spray<5%

Spray orifice

High pressure siphon spray0.4~0.5mm; air spray2.0~3.0mm

Spray pressure

High pressure siphon spray20~30Mpa; air spray0.3~0.4Mpa

Tool washing

Galvanized Plate Special Primer diluent

Film coating thickness

Wet film 100μm, dry film 60μm

Coating interval

Substrate temperature

5℃

20℃

30℃

The shortest

24h

16h

8h

The longest

Unlimit

Surface treatment

The surface of steel material or galvanized plate shall be conducted the process of blasting or sand blasting ,meeting the Swedish derusting standard Sa2.5 level

Construction condition

The substrate temperature must over 3℃ than usual ,relative humidity shall be less than 85%; when constructional substrate temperature is less than 5℃, construction shall be banned.

Finishing paint

Epoxy resin paint, epoxy asphalt paint, chlorinated rubber paint, acrylic resin paint, Acrylic resin paint, phenolic resin paint, chlorosulfonated polyethylene paint, high chlorinated polyethylene paint, etc.

Packing Specification

Rusty red :Component A:20 liters containers can load 25kg components Component B: 4 liters containers can load 1.5kg components

Gray:Component A:20 liters containers can load 24kg components Component B: 5 liters containers can load 4kg components

Considerations

Dry spray phenomenon happened easily in the execution of construction in high temperature season, diluents shall be added, it shall be adjusted to the no sprayed condition.

Safety guide

Avoiding inhalation of vapor or mist, skin and eyes shall not be contacted with this product. In the process of construction, the forced ventilation shall be provided especially in the place which is in narrow and stagnant air condition. The protective gear shall be provided in the execution of construction.

Annotation

＊Above-said thickness of dry film and wet film refers to the index while implementing the high-pressure air-free spray;

＊Relevant data in this instruction is obtained from laboratory, the actual product may be slightly different from it;

＊If above data is changed, the data is based on the latest instruction, without prior notification.